化學(xué)成份
| 合金牌號 |
C |
Cr |
Ni |
Fe |
Mo |
W |
Cu |
AL |
Ti |
Nb |
V |
Co |
SI |
Mn |
P |
S |
| H.B-3 |
≤0.05 |
≤1.00 |
余量 |
4.0~6.0 |
26.0~
30.0 |
|
|
|
|
|
0.20~
0.40 |
≤2.5 |
≤1.00 |
≤1.00 |
≤0.30 |
≤0.03 |
| H.C276 |
≤0.08 |
14.5~16.5 |
余量 |
4.0~7.0 |
15.0~
17.0 |
3.0~
4.5 |
|
|
|
|
≤0.35 |
≤2.5 |
≤1.00 |
≤1.00 |
≤0.04 |
≤0.03 |
| INCONEL 600 |
≤0.15 |
14.0~17.0 |
余量 |
6.0~10.0 |
|
|
≤0.50 |
|
|
|
|
|
≤0.50 |
≤1.00 |
≤0.03 |
≤0.015 |
| INCONEL 625 |
≤0.10 |
20.0~23.0 |
余量 |
≤5.0 |
8.0~
10.0 |
|
|
≤0.40 |
≤0.40 |
3.15~
4.15 |
|
≤1.0 |
≤0.50 |
≤0.50 |
≤0.015 |
≤0.015 |
| INCONEL800 |
≤0.10 |
19.0~23.0 |
30.0~35.0 |
余量 |
|
|
≤0.75 |
0.15~
0.60 |
0.15~
0.60 |
|
|
|
≤0.50 |
≤1.00 |
≤0.03 |
≤0.015 |
| INCONEL825 |
≤0.05 |
19.5~23.5 |
38.0~45.0 |
余量 |
2.5~
3.5 |
|
1.5~
3.0 |
≤0.20 |
0.60~
1.20 |
|
|
|
≤0.50 |
≤1.00 |
≤0.03 |
≤0.030 |
| MONEL400 |
≤0.20 |
|
余量 |
2.0~3.0 |
|
|
≤31.5 |
|
|
|
|
|
≤0.20 |
1.2~1.3 |
≤0.02 |
≤0.010 |
| MONEL500 |
≤0.10 |
|
余量 |
1.00 |
|
|
≤29.5 |
2.70 |
|
|
|
|
≤0.20 |
≤0.80 |
≤0.005 |
≤0.005 |
| M-30C |
≤0.20 |
|
余量 |
2.0~3.0 |
|
|
≤31.5 |
|
|
|
|
|
≤0.20 |
1.2~1.3 |
≤0.02 |
≤0.010 |
機械性能
| 合金牌號 |
熱處理規(guī)范及溫度(℃) |
機械性能 |
適用范圍 |
| 固溶處理 |
抗拉強度(MPa) |
屈服強度(MPa) |
伸長率 |
硬度 |
適用介質(zhì) |
適用溫度 |
| H.B-3 |
1140~1190 |
690 |
310 |
40 |
≤187HB |
耐強還原性腐蝕介質(zhì),如熱濃鹽酸,硫酸，磷酸及氯化氫氣體等 |
≤371℃ |
| H.C276 |
1160~1210 |
690 |
315 |
30 |
≤187HB |
耐鹵蔟及其化合物腐蝕,如乙烯，氯化物，氫氟酸等 |
≤538℃ |
| INCONEL 600 |
1000~1050 |
550 |
240 |
30 |
≤160HV |
耐高溫氧化物介質(zhì) |
-240～650℃ |
| INCONEL 625 |
1100~1150 |
690 |
275 |
30 |
|
耐氧化-還原復(fù)合介質(zhì)，耐海水腐蝕，且熱強度高 |
-240～650℃ |
| INCONEL800 |
1000~1060 |
515 |
205 |
30 |
|
抗氧化性介質(zhì)腐蝕，高溫下抗?jié)B碳性良好 |
-240～650℃ |
| INCONEL825 |
1000~1050 |
590 |
240 |
30 |
|
耐氧化物應(yīng)力腐蝕及氧化-還原復(fù)合介質(zhì)腐蝕(多種離子的硫酸環(huán)境) |
-240～650℃ |
| MONEL400 |
|
482 |
172 |
22 |
|
堿、鹽、食品、不含空氣的酸溶液，氫氟酸等 |
-240～482℃ |
| MONEL500 |
|
565 |
205 |
20 |
|
-240～482℃ |
| M-30C |
|
480 |
220 |
25 |
|
-240～482℃ |
材料牌號對照表
| 中國 |
美國ASTM |
| 0Ni65Mo28F35V(NS321) |
Hastelloy B |
| 0Cr15Ni60Mo16W5Fe5(NS333) |
Hastelloy C |
| 1Cr15Ni75Fe8(NS312) |
Inconel 600(N06600) |
| 0Cr20Ni65Mo10Nb4(NS336) |
Inconel 625(N06625) |
| 0Cr20Ni32AlTi(NS111) |
Inconel 800(N08800) |
| 0Cr21Ni42Mo3Cu2Ti |
Inconel 825(N08825) |
注：除MONEL材料外，其余材料化學(xué)成分及機械性能來源于GB/T15007-94和GB/T15008-94
|